It is evident that the optimal thermal properties are exhibited by the lightweight material. This metal replacement is characterised by its genuine composition and possesses remarkable properties. It is evident that PEEK CF is capable of being anealed. Weight: 0.75 kg.
| SUGGESTED PRINT SETS (1) |
| Suggested print sets | unit | value | test method |
| extruder temp | C° | 390°-420° | internal |
| plate temp | C° | 90° | internal |
| min. nozzle diameter | mm | 0,5 | internal |
| fan | % | 0-05 | internal |
| print speed | mm/1° | 35 | internal |
| PROPERTY |
| Physical | | | |
| Specific gravity | g/cm3 | 1.36 | ISO 1183-3 |
| Water absorption at equilibrium | % | <0,1 | ISO 62 |
| Linear mould shrinkage | % | 0,2/0,4 | DIN 16742 |
| Mechanical at 23°C / 50% rh | | | |
| Tensile strength | MPa | 126 | ISO 527 |
| Elongation at maximum force | % | 3,9 | ISO 527 |
| Modulus of elasticity | GPa | 7,8 | ISO 527 |
| Charpy impact strength | kJ / m2 | 66 | ISO 179 1eU |
| Charpy impact strength, notched | kJ / m2 | 7 | ISO 179 1eA |
| Thermal | | | |
| Heat distortion temp. | °C | 280 | ISO 75 |
| Continuous service temp. | °C | 250 | IEC 60216 |
| Service temp. | °C | 280 | lifetime max. 200h |
| Electrical | | | |
| Insulation resistance strip electrode | Ω | ≤109 | DIN/IEC 60167 |
| Surface Resistance | Ω | ≤109 | DIN IEC 60093 |